TopesterTM 4系列是一类共聚酯类热塑性弹性体。该系列产品可广泛应用于汽车、工业、电线电缆、消费品、聚合物改性等领域,该系列产品适合挤出和注塑加,并且可以完全回收利用。
TopesterTM 4 Series |
Color | Durometer | Density | Melt Index@ 230oC/2.16kg | Flexual Modulus | Tensile Stress @ Break | Elongation @ Break | Charpy Notched Impact Strength (230C) | Charpy Notched Impact Strength (-300C) | Melting Temperature | Vicat Softening Temperature, 10N | Volume Resistivity | Water Absorption, 24hr | Shrinkage | Injection Molding | Extrusion | Blow Molding |
ISO 868 | ISO 1183 | ISO 1133 | ISO 178 | ISO 527 | ISO 527 | ISO 179 | ISO 179 | ISO 11357 | ISO 306 | IEC 60093 | ISO 62 | ISO 294 | |||||
Shore D | g/cm3 | g/10min | MPa | MPa | % | KJ/m2 | KJ/m2 | 0C | 0C | Ohm*cm | % | % | |||||
商品名 | 颜色 | 硬度 | 密度 | 熔融指数 | 弯曲模量 | 拉伸强度 | 断裂伸长率 | 常温简支梁缺口冲击强度 | 低温简支梁缺口冲击强度 | 熔融温度 | 维卡软化温度 | 体积电阻率 | 吸水率 | 收缩率 | |||
428RM | Natural | 28 | 1.07 | 16 | 30 | 18.0 | 940 | No break | No break | 170 | 80 | 1.0E+12 | 0.7 | 1.1 | √ | √ | |
435RM | Natural | 35 | 1.10 | 10 | 55 | 20.0 | 850 | No break | No break | 192 | 132 | 2.0E+12 | 0.6 | 1.2 | √ | √ | |
440RM | Natural | 40 | 1.13 | 10 | 80 | 23.0 | 760 | No break | No break | 202 | 140 | 5.0E+12 | 0.5 | 1.3 | √ | √ | |
445RM | Natural | 45 | 1.15 | 10 | 100 | 26.0 | 690 | No break | No break | 210 | 155 | 1.0E+13 | 0.5 | 1.4 | √ | √ | |
455RM | Natural | 55 | 1.19 | 10 | 220 | 37.0 | 590 | No break | No break | 204 | 180 | 4.0E+13 | 0.4 | 1.5 | √ | √ | |
455RL | Natural | 55 | 1.19 | 19 | 220 | 36.0 | 570 | No break | No break | 204 | 180 | 4.0E+13 | 0.4 | 1.6 | √ | √ | |
463RM | Natural | 63 | 1.22 | 12 | 320 | 40.0 | 480 | No break | 18 | 212 | 195 | 9.0E+13 | 0.3 | 1.6 | √ | √ | |
472RM | Natural | 72 | 1.26 | 13 | 550 | 42.0 | 370 | 15 | 9 | 219 | 205 | 1.0E+14 | 0.3 | 1.7 | √ | √ | |
440CB | Natural | 40 | 1.13 | 1 | 85 | 24.0 | 610 | No break | No break | 202 | 140 | 2.0E+12 | 0.5 | 1.3 | √ | √ | |
445CB | Natural | 45 | 1.15 | 1 | 110 | 27.0 | 530 | No break | No break | 210 | 155 | 8.0E+12 | 0.5 | 1.4 | √ | √ | |
450CB | Natural | 50 | 1.18 | 1 | 170 | 33.0 | 340 | No break | No break | 202 | 165 | 2.0E+13 | 0.4 | 1.3 | √ | √ |